Ni 99.0 C 0.15 Cu 0.25 Fe 0.40 Mn 0.35 Si 0.35 S 0.01
High Performance Alloys stocks and produces this grade in the following forms: Bar, wire, sheet, plate, coil, fasteners and forgings.
Commercially pure wrought Nickel with good mechanical properties over a wide range of temperature and excellent resistance to many corrosives, in particular hydroxides.
Good resistance to corrosion in acids and alkalis and is most useful under reducing conditions. Outstanding resistance to caustic alkalis up to and including the molten state. In acid, alkaline and neutral salt solutions the material shows good resistance, but in oxidizing salt solutions severe attack will occur. Resistant to all dry gases at room temperature and in dry chlorine and hydrogen chloride may be used in temperatures up to 550C. Resistance to mineral acids varies according to temperature and concentration and whether the solution is aerated or not. Corrosion resistance is better in de-aerated acid.
Ni
C
Mn
Cu
S
Si
Fe
Max
0.15
0.35
0.25
0.01
0.40
Min
99.0
Ultimate Tensile
Yield Strength (0.2% OS)
Elong.
R/A
Hardness
Cold Worked
75 KSi
50 KSi
15
515 MPa
345 MPa
Hot Worked
55 KSi
15 KSi
40
380 MPa
105 MPa
Form
Standard
Metal Type
UNS N02200
Bar
ASTM B160 Din 17752 BS 3076
Wire
Sheet
ASTM B162 Din 17750 BS 3072
Plate
Fitting
ASTM B366
Forging
ASTM B564
Weld Wire
ERNi-CI